Iran 2102TX00 Blown Film Grade LDPE | High Flow & High Clarity Imported Special Material for Thin-Wall Films
Product Overview
Iran 2102TX00 is a blown film grade LDPE manufactured by Arya Sasol Petrochemical with proprietary SABTEC tubular polymerization technology. Slip agent, anti-block agent and antioxidant stabilizer are pre-formulated inside the pellets. It delivers balanced melt flow and solid melt strength for steady bubble forming and a wide processing window. The material produces ultra-transparent thin films with haze as low as 2.8%, featuring soft touch, outstanding toughness and long-term anti-aging performance. It complies with food contact regulations and suits mass production of premium laundry bags and textile packaging films. Supported by steady supply from the Middle East, it delivers remarkable cost performance for film manufacturers.
1. Basic Product Specifications
All listed figures are typical values for reference only, tested on standard 30μm blown film specimens.This product is made of 100% virgin uniform milky white pellets, free of black spots, impurities and irregular particles to guarantee consistent quality across every batch. Goods come in original 25kg factory bags, and a batch-specific COA is supplied to realize full-track quality inspection.
Density: 0.920 g/cm³ (ISO 1183)
Melt Flow Rate (190°C/2.16 kg): 4.7 g/10min (ASTM D1238)
Haze: ≤3.2% (30 μm film, typical value: approx. 2.8%)
Dart Impact Strength: 150 g (25 μm film, ASTM D1709)
Longitudinal Tear Strength: 80 kN/m (ISO 6383-2)
Transverse Tear Strength: 25 kN/m (ISO 6383-2)
Longitudinal Elongation at Break: >1000%
Transverse Elongation at Break: >500%
Specification Note: The obvious difference between longitudinal and transverse elongation at break is an inherent physical property of tubular polymerization process, which will not affect normal film production.
Vicat Softening Temperature: ≥88°C
Melting Point: 108–113°C
2. Core Product Advantages
Pre-mixed functional additives for smooth film unwinding without adhesion
Slip agent, anti-block agent and antioxidant stabilizer are fully blended at factory, so no extra additives are required during processing. Low additive migration keeps film surface clean, supporting stable printing and lamination while reducing surface blooming defects and simplifying downstream production steps.
Ample melt strength matching high-speed ultra-thin film production lines
Balanced melt flow and even long-chain branched structure maintain steady bubble shape and uniform film thickness, lowering the chance of bubble rupture. It works perfectly for 12–50μm ultra-thin films on both standard and high-speed blown film machines. Its 150g dart impact strength upgrades film toughness and overall production yield.
Ultra-high transparency paired with balanced toughness, cold resistance and UV stability
Finished films carry high gloss and minimal crystal spots with superior clarity. The material retains stable tear and impact resistance under low-temperature conditions. Built-in anti-aging stabilizers slow yellowing for indoor storage; long-term outdoor exposure requires additional UV masterbatch blending to resist photo-oxidation aging.
Stable imported raw material supply and broad material compatibility
Manufactured by Arya Sasol Petrochemical, this LDPE enjoys steady supply from the Middle East. The low-odor resin meets food contact standards and resists acid & alkali corrosion. It can be blended with LLDPE to adjust film rigidity and toughness to fit various packaging scenarios.
3. Main Application Fields
Food Packaging Films: Fresh food storage bags, transparent outer packaging for snacks, small heat-sealed packaging pouches.
Textile & Laundry Packaging Films: Clear laundry bags, garment packaging films, lamination films for home textiles
Daily Commodity Packaging Films: Zipper storage bags, lightweight shopping bags, outer wrapping films for daily chemical goods.
Other Applications: Base resin for high-end thin film production. It can be blended with LLDPE to adjust film rigidity and toughness as modification raw material.
4. Processing & Storage Guidelines
Processing Parameters
Barrel Temperature: 145–160°C
Special Reminder: This LDPE supports a low-temperature extrusion window to reduce power consumption. Adjust parameters according to actual equipment conditions to prevent melt degradation caused by overheating.
Die Temperature: 170–190°C
Blow-up Ratio: 2.0–3.0, adjust based on real production needs
Frost Line Height: 5–7 times of die diameter
Drying Requirement: Normally stored pellets require no drying treatment. Dry damp pellets at 60–70°C for 1 hour and cool to room temperature before feeding.
Storage Requirements
Store pellets in cool, dry and well-ventilated warehouses. Keep away from open fire, rainwater, direct sunlight and odorous articles to avoid moisture absorption and odor contamination. Pallet stacking height cannot exceed 5 layers. The shelf life lasts 2 years under standard storage conditions.
5. Quality Assurance & Supply Service
All supplied pellets are 100% genuine virgin Iran 2102TX00 LDPE sourced from Arya Sasol Petrochemical. Original batch COA documents are provided for full index inspection. We maintain sufficient imported spot stock all year round, supporting free sample testing, small trial orders, full-truck and full-container bulk shipments. Professional technical support is available to satisfy diversified production and procurement demands of film manufacturers.
6. Frequently Asked Questions
Q1: What processing strengths does Iran 2102TX00 have compared with ordinary LDPE grades?
A: This resin features high melt flow and a dedicated low-temperature processing formula, cutting power consumption and preventing material degradation. It produces minimal additive precipitation, eliminating roller sticking and film blooming during long-term continuous high-speed production.
Q2: What is the minimum film thickness this resin can produce steadily? Can thickness deviation be well controlled?
A: It supports stable production of ultra-thin films between 12μm and 50μm. Sufficient melt strength stabilizes bubble status with tiny fluctuation, greatly reducing longitudinal and transverse thickness deviation and lifting finished product yield.
Q3: How is the film’s performance for post-printing and lamination procedures?
A: Low additive migration leaves film surfaces free of precipitates, delivering strong ink adhesion and stable lamination bonding effect. It fits regular printing and dry lamination without extra corona treatment, showing outstanding adaptability for secondary processing.
Q4: What blending ratio is recommended when mixing this LDPE with LLDPE?
A: The suggested proportion ranges from 10% to 30% for common film production. This blend improves LLDPE melt fluidity, stabilizes bubble forming, optimizes film transparency and softness, and balances overall rigidity and toughness.
Q5: Is the raw material supply stable? Can you handle urgent delivery orders?
A: We hold long-term stable spot inventory of original Middle Eastern raw materials with no stockout risks. We accept sample orders, emergency replenishment and full-load bulk delivery, paired with all-round professional technical follow-up to meet clients’ urgent production needs.
7. Product Summary
Iran 2102TX00 is a high-flow, high-clarity blown film LDPE complete with pre-mixed functional additives. It delivers stable bubble forming, excellent low-temperature toughness and UV resistance, and complies with food contact standards to fit high-speed ultra-thin film production. Backed by reliable Middle East supply, it is a cost-effective raw material choice for laundry bags, textile wrapping films and lightweight food packaging films.
Please contact us for full technical datasheets, compliance certificates, official COA reports, free samples and competitive bulk quotations.